Leather Splitter?

[J Hayes]

Let us know how it comes out. I do think even the old ones started life in the 15-17degree range, over the years I could see how someone would just grind the leading edge slowly increasing the angle over the years. Both my CS and HF Osborne were ground nearly all the way to the spine leaving maybe a 1/4" of flat on the top.

Keep track of what it takes you to make that blade, I'd bet you could sell a few

[deloid]

I will make a few blades out of my O1 stock. I have the length and slot from my present 84. I measure 3/8th inch thickness and perhaps I should keep it there if that is what the Osborne 84s were supposed to have. I don't know what the original width was due to wear on my now pretty much exhausted blade. Any help with this?

[J Hayes]

My old HF Osborne is 1.38" and .427" thick, the new Weaver is 1.86" if that helps at all. The HF is over 100 years old and is likely much shorter than it was when new. My guess is the blade Bruce will be getting from Osborne will be about 1.75", now we just wait in suspense for him to report back.......

Edited September 13, 2014 by J Hayes

[deloid]

Thank you so very much! I was guessing that adding the original lines and width would come to around 1.75" but it's nice to read this from you. Yes, Bruce will undoubtedly know.

[deloid]

I have been reflecting on the blade design and now I think I see a purpose to the lower carbon steel weld. I suspect that the vibrations from pulling on certain tough leather may transmit too harshly to the cast frame. Mild steel would soften these vibrations and also render the attachment (nut to frame)less prone to damage. Theoretically at least.

If so, I can forge weld wrought to the tool steel. Unfortunately I have a limited supply of wrought iron.

[StrigaMort]

I'm very interested in reading this. I'm especially interested in watching what happens with your blade design Dean. Leather is my primary concern, but I come to leather directly from the knife world. I have the means to heat treat simple eutectoid steel (1080/84) properly, so your experience with o1 will be fun to watch. Please keep us updated.

[deloid]

I'll certainly let you know on this forum. I too started with forging then stock removal. I am still a member of the ABS our local Idaho Knife Association and the CKCA. My wife has taken the leather business to new wonderful heights and while I love helping as I can I have been pulled from my primary interests. This is at least one way that I can get back to working metal. perhaps I might sneak in a couple of hunters and the 9 1/4 inch flat grind Gents bowie that used to drive me nuts (getting the grind right).

It's funny, I first started making knife sheaths because I made knives and more importantly, Paul Long gave me his time and attention to get me started correctly. From there I made a belt for my wife. This inspired her and she took on the work herself with drive, passion and creativity. Now I assist and troubleshoot.

Thanks for your expressed interest!

Dean

[StrigaMort]

Hey that's cool. Small world. I bug Paul at least once a day (ears burning Paul?) over on Bladeforums. I know he's here as well, although I don't think I've bumped into him.

You ever get some time, stop by and say hi, I'd love to see your work. Obviously some of the leather guys at BF are also knife makers. I dabble in both, but sheaths are what keep me busy.