Leather Weight for Lined Holsters.

[Latigo Smith]

I've just made an account on this website, as I'm just now getting back into leatherwork after many years of being away from it due to far too many other projects. Years ago, the holsters I made were unlined, but I plan to make my holsters lined with veg-tan going forward. Once I get back in the groove of it (as I'm a tad rusty, I'm sure), I'll also be making holsters to sell as a business venture. I have a few questions regarding the optimal weight of leather to use for such a purpose. For reference, I'll be making holsters primarily for full size handguns such as the Colt Gov't .45 and Super .38, Browning Hi-Power, Browning Sig BDA .45, Smith 59, Smith N-Frames, Colt Python and also some medium frame revolvers such as Ruger Security, Service and Speed Six's, Smith K-Frames as well as Colt Mk. III's and Official Police.  As such, I'm looking for a leather weight that will provide good stiffness to firmly support the handgun and that will not allow the gun to flex the holster with use, yet while still being able to, with some effort, achieve good detail molding to relieve pressure off the high edges of the gun for the purpose of helping to preserve bluing. 

 

I've read from many members on this site that a lined holster consisting of 2 layers of equal weight veg-tan laminated with a good contact cement such as Weldwood will be stiffer and more rigid than an unlined holster of similar thickness. As such I was planning on using two layers of 4/5oz for this purpose, as I tend to like 8/9oz or 9/10oz for an unlined holster, depending on the size and weight of the gun.

 

However, I read something from a man whose expertise I trust which stated that the opposite is the case, meaning that a lined holster will be softer and less rigid than an unlined holster of similar thickness due to the leather's temper. It's from a 1981 article titled "Holster Linings: Hidden Protection", written by Richard D.E. Nichols, the former head of R&D at Bianchi International.  Here's the quote;

"The cowhide lined holster has more body, stiffness and rigidity than the suede lined or unlined holster. It also tends to be the bulkiest of the three. Because of a leather property called temper, a lined holster is not merely two thin layers that equal an unlined holster's thickness. A heavy duty unlined holster might be made of 10 ounce leather, which is around 3/16" thick. However, comparable cowhide lined holsters would be two layers of 7 ounce, which is a bit less than 1/4" thick. The difference is caused by leather's tendency to become stiffer as it's made thicker. This stiffness or temper equates to body for the holster. Using the above example again, two layers of 5 ounce might be the same thickness as the single piece of 10 ounce, but would be much softer and less durable."

 

 

I have a tendency to trust Mr. Nichols' advice, given that he has likely created more successful holsters designs than any other one person, between his 17 years at Bianchi during the companies' peak and his design work for many other gunleather companies in the 38 years since Bianchi was sold. Yet, I also trust the advice of many of the members on this website.

 

I've considered the possibility that the cause for this difference of experiences with lined holsters could be the adhesive used to laminate the two layers of leather together. In the article mentioned above, there's a photograph of a lined holster having glue applied to it's layers at the Bianchi factory, and while it's difficult to accurately identify the type of glue being used, it appears to be of a thinner and smoother consistency than contact cement, and as such I'm wondering if they used a glue that's less stiff and rigid than contact cement once cured. I'll be attempting to contact Mr. Nichols shortly for the purpose of asking him what glue they used at Bianchi, but until then it's just a guess.

 

I'd be appreciative for the opinions on this matter from the kind people of this forum. In particular, I'd be very interested to hear the opinion of Mr. Dwight, whom I know for a fact makes quite a number of lined holsters. I know the smartest option is to experiment with making lined holsters using different weight leathers to determine which will work best. But, I'd still like to have a general idea of what weight I should be using beforehand just to get me in the ballpark. Thank you. 

[chuck123wapati]

my two cents.

The temper of a given piece of leather is affected by numerous variables, including the Type of cow, tanning processes/tannery, and where it is taken from on the hide (i.e., belly or back), and construction techniques are just a partial list of the possibilities. So to make an absolute statement on which is stiffer is silly at best. Given that you want a guaranteed optimal outcome, you will have to do some real-life testing to eliminate as many of those variables as possible. Use specific parts of the hide, specific tannery's, and be very precise with your construction, including the addition of liquors/oils during the finishing stages. Some folks use a thick outer layer with a thin liner, some use two equal-thickness pieces because they can get them from the same hide, thinking it makes construction costs less or easier in some way. Whether one method is better is again debatable and susceptible to the variables. Bianchi probably can handle the cost of more waste than you at the beginning, so they can get refined and consistent results. we, as small batch folks, need to be much more selective to compete.

Contact cement can be diluted and made thinner with acetone. Bianchi probably figured out it goes farther and dries faster that way.

Good luck to you. I can't wait to see your stuff.

[AlZilla]

Red Nichols, as I recall, recommends horse butt strips. I've been trying to find the post over on the Smith & Wesson forum where he talked about it. I'll keep looking.

[wizard of tragacanth]

Welcome to the forum! Interesting first post.

There are many factors affecting the stiffness of the finished project. I have often wondered about the mineral content of the water that is used for wet forming, e.g. high minerals vs distilled? I have never tested this though. So, lazy!